EFFECT OF MODIFIERS ON RHEOLOGICAL AND THERMAL PROPERTIES OF BOROSILICATE GLASSES
Abstract
Results of research for the glass system Na2O-K2O-B2O3-SiO2 at 2:1 molar ratio of K2O/Na2O modifiers are presented. It has been found that increasing (K2O+Na2O)/B2O3 ratio in glass compositions leads to higher low-temperature viscosity and viscosity gradient in the range of 109-104Pa-s. The established temperature dependences of viscosity allow to optimize borosilicate glass compositions with predetermined characteristics, as well as technological parameters of their synthesis and formation.
About the Authors
I. A. Levitski
Belarusian State Technological University
Беларусь
Беларусь
L. F. Papko
Belarusian State Technological University
Беларусь
Беларусь
M. V. Dyadenko
Belarusian State Technological University
Беларусь
Беларусь
References
1. Аппен, А. А. Химия стекла / А. А. Аппен. – Л.: Химия, 1974. – 351 с.
2. Двухфазные стекла: структура, свойства, применение / О. В. Мазурин [и др.]. – Л.: Наука, 1991. – С. 128–135.
3. Левицкий, И. А. Влияние состава и структурных факторов на вязкость боросиликатных стекол и расплавов / И. А. Левицкий, Л. Ф. Папко // Стекло и керамика. – 2010. – № 11. – С. 4–7.
4. Левицкий, И. А. Реологический свойства боросиликатных стекол и расплавов / И. А. Левицкий, Л. Ф. Папко, М. В. Дяденко // Стекло и керамика. – 2013. − № 6. – С. 6−10.
5. Шелби, Дж. Структура, свойства и технология стекла / Дж. Шелби. – М.: Мир, 2006. – 288 с.
Review
Views:
700
JATS XML
Email this article 