Electric conductivity and thermal expansion of highly coercive ferrites Sr1-xSmxFe12-xCoxO19
Abstract
Specific electric conductivity (æ) of Sr1-xSmxFe12-xCoxO19 ferrites has been measured in the 300-1100 K temperature range. It has been determined that conductivity activation energy for Sr1-xSmxFe12-xCoxO19 ferrites ( x = 0-0,5) in the temperature range above the Fracture temperature ( Tfrac) is 0,06-0,14 eV higher than the activation energy in the temperature range below the Tfrac. The coefficient of linear thermal expansion (α) for Sr1-xSmxFe12-xCoxO19 ferrites changes slightly when x is increased: from 1,20·10-5 K-1 for SrFe12O19 to 1,27·10-5 K-1 for Sr0,5Sm0,5Fe11,5Co0,5O19.
About the Authors
Wu Ze
Белорусский государственный технологический университет
Belarus
Belarus
L. A. Bashkirov
Белорусский государственный технологический университет
Belarus
Belarus
S. V. Slonskaya
Белорусский государственный аграрный технический университет
Belarus
Belarus
References
1. Смит Я., Вейн Х. Ферриты. Физические свойства и практическое применение. М.: ИЛ, 1962.
2. Летюк Л. М. и др. Металлургия. М., 1994.
3. Крупичка С. Физика ферритов и родственных им магнитных окислов М.: Мир, 1976. Т. 2.
4. Taguchi H. et al. // 7th International Conference on Ferrites, Bordeaux, 3-6 september 1996 / Bordeaux Convention Center France. Bordeaux, 1996. P. 3-4.
5. Obara J., Yamamoto H. // J. of the Japan Society of Powder and Powder Metallurgy. 2000. Vol. 47, N 7. P. 796-800.
6. Wang J. F. // J. of Alloys and Compounds. 2005. Vol. 403, Iss. 1. P. e104-e109.
7. Башкиров Л. А. и др. // Свиридовские чтения. Минск: БГУ, 2008. С. 100-106.
Review
Views:
451
Email this article 