Synthesis, structure and properties of the solid solutions based on layered calcium cobaltite
Abstract
The (Ca,M)3Co4O9+δ (M = Na, Cu, Pb, Bi) solid solutions have been synthesized, their lattice constants have been determined and their electric conductivity and thermo-EMF were studied in 300-1100 K temperature interval. It has been found that Ca2,8Pb0,2Co4O9+δ solid solution possessed the greatest thermo-EMF coefficient of 0,32 mV/K at 1100 K. Activation energies of electrical conductivity and power factor of ceramics studied have been calculated.
About the Authors
A. I. Klyndyuk
Белорусский государственный технологический университет
Belarus
Belarus
I. V. Matsukevich
Белорусский государственный технологический университет
Belarus
Belarus
References
1. Koumoto K., Terasaki I., Murayama N. (eds.) Oxide Thermoelectrics. Trivandrum, India, Research Signpost. 2002.
2. Fergus J. W. // J. Eur. Ceram. Soc. 2012. Vol. 32. P. 525-540.
3. Zhang Y. F., Zhang J. X., Lu Q. M., Zhang Q. Y. // Mater. Lett. 2006. Vol. 60. P. 2443-2446.
4. Park J. W., Kwak D. H., Yoon S. H., Choi S. C. // J. Ceram. Soc. Jap. 2009. Vol. 117, N 5. P. 643-646.
5. Клындюк А. И., Мацукевич И. В. // Весці НАН Беларусі. Сер. хім. навук. 2012. № 3. С. 11-16.
6. Prevel M., Perez O., Noudem J. G. // Solid State Sci. 2007. Vol. 9. P. 231-235.
7. Клындюк А. И., Мацукевич И. В. // Неорган. материалы. 2012. Т. 48, № 10. С. 1181-1186.
8. Wang Y., Sui Y., Ren P. et al. // Chem. Mater. 2010. Vol. 22. P. 1155-1163.
9. Мацукевич И. В., Клындюк А. И. // Термоэлектричество. 2013. № 3. С. 50-57.
10. Massett A. C., Miche l C., Maignan A. et al. // Phys. Rev. B. 2000-I. Vol. 62, N 1. P. 166-175.
11. Shannon R. D., Prewitt C. T. // Acta Cryst. 1969. Vol. B25. Pt. 5. P. 946-960.
Review
Views: 438
Email this article 