Electrochemical deposition of yellow brass under pulse electrolysis conditions
Abstract
Electrodeposition of copper-zinc alloy of non-cyanide sorbate electrolyte at current densities of 1,0-3,5 A/dm2 allows to produce yellow brass with a copper content of about 63-64 wt.°%. Using pulsed current allows to intensify the process of deposition 1,3-1,6 times and to increase the current efficiency of the alloy by 1,2-4,2 %. Coatings obtained by pulsed electrolysis have fine-grained structure, more compact and with good adhesion to the steel substrate. Imposition of pulsed current allows deposition of homogeneous phase coating and eliminates formation of intermetallic compounds.
About the Authors
E. V. Mihedova
Белорусский государственный технологический университет
Беларусь
Беларусь
V. V. Yaskelchik
Белорусский государственный технологический университет
Беларусь
Беларусь
A. A. Chernik
Белорусский государственный технологический университет
Беларусь
Беларусь
I. M. Zharsky
Белорусский государственный технологический университет
Беларусь
Беларусь
References
1. Седлярова С. Н. // Изв. Гомельского гос. ун-та. 2006. № 5. С. 93-99.
2. Vagramyan Т., Leach J. C. L., Moon J. R. // Electrochim. acta. 1979. Vol. 24, N 2. P. 231-236.
3. Винокуров Е. Г., Кадырин К. Л, Бондарь В. В. // ЖПХ. 2010. Т. 83, вып. 4. С. 606-610.
4. Эль-Шейх Ф. М. // Гальванотехника и обработка поверхности. 2004. Т. 12, № 4. С. 14-23.
5. Поветкин В. В., Захарова М. С., Муслимое Р. Р. // ЖПХ. 1999. Т. 72, вып. 8. С. 1297-1300.
6. Ivani A. Carlos, Moacyr Rodrigo H. de Almeida // J. of Electroanalytical Chemistry. 2004. Vol. 401, N 1. P. 153-159.
7. Хмелев А. В., Федорова Е. А., Головушкина Л. В. // Гальванотехника и обработка поверхности. 2011. Т. 7, № 1. С. 33-37.
8. Костин Н. А., Кублановский B. C. Импульсный электролиз сплавов. Киев: Навук. думка, 1996.
9. Костин Н. А. // Гальванотехника и обработка поверхности. 1992. Т. 1, № 1-2. С. 16-18.
Review
Views:
731
JATS XML
Email this article 